J. Physique Lett. 37, 299-302 (1976)
DOI: 10.1051/jphyslet:019760037011029900

Compressive creep of ultrafine grained MgO polycrystals

J. Crampon¹, A.C.D. Chaklader² et B. Escaig<sup>1

1</sup>  Laboratoire « Structure et propriétés de l'état solide », Université des Sciences et Techniques de Lille, Villeneuve-d'Ascq, France
²  Department of Metallurgy, University of British Columbia, Vancouver 8, U. S.A.

Abstract
Steady state compressive creep of ultrafine-grained MgO has been studied in the temperature range 0.3 to 0.38 Tm. The specimens were fabricated by reactive hot pressing i.e. by hot-pressing of Mg(OH)2 during the decomposition reaction, which produced dense specimens (90 % of the theoretical density) with 1 000 Å average grain size. The value of the stress exponent was found to be unity and the activation enthalpy was of the order of 36 kcal/mole.

Résumé
Le fluage stationnaire de l'oxyde de Magnésium polycristallin à grains ultra-fins a été étudié entre 0,3 et 0,38 Tm. Les échantillons ont été fabriqués par frittage réactif durant la réaction de décomposition de Mg(OH)2 . Ce type de frittage produit un matériau dense (90 % de la densité théorique) possédant une taille de grains très fine (1 000 Å). La sensibilité de la vitesse de fluage stationnaire avec la contrainte s'exprime par un exposant de contrainte de l'ordre de l'unité et l'enthalpie d'activation est faible de l'ordre de 36 kcal/mole.

PACS
6220H - Creep.
8140L - Deformation, plasticity and creep.

Key words
ceramics -- creep -- hot pressing -- magnesium compounds -- ultrafine grained MgO polycrystals -- compressive creep -- reactive hot pressing -- decomposition reaction -- stress exponent -- activation enthalpy