J. Physique Lett. 38, 259-262 (1977)
DOI: 10.1051/jphyslet:019770038013025900

Propriétés optiques de MnAu2

Ch. Jung et M. Ph. Stoll

Laboratoire Pierre-Weiss , 5, rue de l'Université, 67084 Strasbourg, France

Abstract
By means of a polarimetric method, the optical constants of MnAu2 between 0.5 and 3.5 eV were determined. Intraband absorption is dominant below 1 eV ; with m* = 2.06 m0 and τ = 2.4 × 10-15 s. Interband processes become evident from 1 eV upwards and a parabolic edge, observed at 2.17 eV, is attributed to transitions from the top of the gold d band toward the Fermi level. The occupied states of the manganese are thought to be situated around 1 eV. The high effective mass suggests the presence of a manganese d sub-band around E F.

Résumé
On a déterminé par une méthode polarimétrique les constantes optiques de MnAu2 entre 0,5 et 3,5 eV. L'absorption intrabande est dominante en-dessous de 1 eV ; avec m* = 2,06 m0 et τ = 2,4 × 10-15 s. Le processus interbandes se manifeste à partir de 1 eV et on a mis en évidence un seuil parabolique à 2,17 eV qu'on attribue aux transitions issues du sommet de la bande (d) de l'or vers le niveau de Fermi. Les états (d) occupés du manganèse seraient situés autour de 1 eV. La masse effective élevée suggère la présence d'une sous-bande (d) du manganèse autour de EF.

PACS
7820D - Optical constants and parameters condensed matter.
7830E - Infrared and Raman spectra in metals.
7840K - Visible and ultraviolet spectra of metals, semimetals, and alloys.

Key words
gold alloys -- infrared spectra of inorganic solids -- manganese alloys -- optical constants -- visible and ultraviolet spectra of inorganic solids -- polarimetric method -- optical constants -- MnAu sub 2 -- parabolic edge -- Fermi level -- high effective mass -- 0.5 to 3.5 eV -- intraband absorption -- interband processes -- Au band -- Mn d subband