J. Physique Lett. 42, 491-493 (1981)
DOI: 10.1051/jphyslet:019810042022049100

Internal friction in amorphous polystyrene at low temperature and high frequency

J.Y. Duquesne et G. Bellessa

Laboratoire de Physique des Solides, Université Paris-Sud, 91405 Orsay, France

Abstract
The existence in polystyrene of an internal-friction peak around 80 K at 50 MHz is reported. This peak displays many similarities with the peak observed in amorphous selenium. It is interpreted in the frame of the same model. We explain our results with thermal activated relaxation processes displaying a constant distribution of barrier heights between 0 and 600 K. We suggest that the observed peak is the resolution at high frequency of the ε-shoulder which has been reported previously at much lower frequency.

Résumé
Nous présentons l'observation, dans le polystyrène, d'un pic de frottement interne localisé autour de 80 K à 50 MHz. Ce pic présente beaucoup de similitudes avec celui observé dans le sélénium amorphe et est interprété dans le cadre du même modèle. Nous expliquons nos résultats à l'aide de processus de relaxation par activation thermique dont les énergies sont distribuées de façon constante entre 0 et 600 K. Nous suggérons que le pic observé est la résolution à haute fréquence de l'épaulement ε qui a été observé précédemment à beaucoup plus basse fréquence.

PACS
6240 - Anelasticity, internal friction and mechanical resonances.
8140J - Elasticity and anelasticity.

Key words
internal friction -- polymers -- 2 to 600K -- amorphous polystyrene -- internal friction -- 50 MHz -- thermal activated relaxation -- barrier heights