Observation of new X-ray diffuse scattering features in FeNb3Se 10

R. Moret¹, J.P. Pouget¹, A. Meerschaut² et L. Guemas<sup>2

1</sup>  Laboratoire de Physique des Solides, bât. 510 and LURE, bât. 209 C, Université Paris-Sud, 91405 Orsay, France
²  Laboratoire de Physico-chimie des Solides, Université de Nantes, 44072 Nantes, France

Abstract
We present the results of an X-ray diffuse scattering study of FeNb 3Se10 using both standard and synchrotron radiations. New diffuse scattering features in the form of rods with reduced wave vectors (0.5, 0.33, l) have been observed. Their intensity grows as the temperature is reduced but the diffuse character is preserved down to 20 K though intensity modulations are present. These results call for a careful structural re-investigation of this compound.

Résumé
Nous présentons les résultats d'une étude par diffusion diffuse des rayons X de FeNb3Se10. Le rayonnement synchrotron a été utilisé conjointement avec les sources standard. Des lignes diffuses de vecteur d'onde (0,5, 0,33, l) ont été mises en évidence. Leur intensité augmente quand la température décroît, mais elles restent diffuses, quoique modulées, jusqu'à 20 K. Ces résultats devraient initier de nouvelles études structurales pour ce composé.

PACS
6160 - Crystal structure of specific inorganic compounds.
7130 - Metal insulator transitions and other electronic transitions.

Key words
crystal atomic structure of inorganic compounds -- iron compounds -- metal insulator transition -- niobium compounds -- X ray scattering -- synchrotron radiation -- structural properties -- X ray diffusion scattering -- FeNb sub 2 Se sub 10 -- intensity modulations