Frottement intérieur hautes températures d'un aluminium de haute pureté

C. Esnouf, M. Gabbay et G. Fantozzi

I.N.S.A. de Lyon, Groupe d'Etudes de Métallurgie Physique et de Physique des Matériaux , Bâtiment 502, 20, avenue A.-Einstein, 69621 Villeurbanne Cedex, France


Abstract
We have observed in high purity (6 N) polycrystalline aluminium an internal friction peak situated around 0.5 TF (TF = melting point K). The peak height is large (δmax is about 0.1) and its temperature is sensitive to the vibration amplitude. This peak, very stable during annealing, is similar to the P1 peak observed by Woirgard and can be attributed to the dislocation glide controlled by jog climbing.


Résumé
Nous avons mis en évidence dans un aluminium polycristallin de haute pureté (6 N) un pic de frottement intérieur situé vers 0,5 TF (TF = température de fusion en K) dont l'intensité est importante (δmax est de l'ordre de 0,1) et dont la position est sensible à l'amplitude de déformation de mesure. Ce pic, très stable lors des recuits, peut être assimilé au pic P1 observé par Woirgard et attribué au glissement des dislocations contrôlé par la montée des crans.

PACS
6170L - Slip, creep, internal friction and other indirect evidence of dislocations.
6240 - Anelasticity, internal friction and mechanical resonances.
8140J - Elasticity and anelasticity.

Key words
aluminium -- annealing -- dislocation climb -- dislocation jogs -- internal friction -- slip -- internal friction -- vibration amplitude -- annealing -- dislocation glide -- jog climbing -- polycrystalline Al