J. Physique Lett. 42, 295-299 (1981)
DOI: 10.1051/jphyslet:019810042013029500

EPR study of the cis-trans isomerization process in polyacetylene films

P. Bernier¹, C. Linaya², M. Rolland¹ et M. Aldissi<sup>2

1</sup>  Groupe de Dynamique des Phases Condensées, USTL, place Eugène-Bataillon, 34060 Montpellier, France
²  Laboratoire de Chimie Macromoléculaire, USTL, place Eugène-Bataillon, 34060 Montpellier, France

Abstract
Using EPR we have studied the isomerization process converting cis-(CH) x films to the trans form upon thermal treatment. Following the measured linewidth and number of spins versus time and temperature, it is shown that for the lowest temperatures (T < ˜ 140 °C) isomerization cannot be complete while for the highest ones (T > ˜ 200 °C) degradation becomes more and more efficient. There exists a small temperature range ( T ˜ 140-150 °C) where optimal characteristics (total isomerization + small degradation) can be achieved.

Résumé
En utilisant la RPE nous avons étudié le processus d'isomérisation qui conduit, par traitement thermique, des films de cis-(CH)x à la configuration trans. En suivant les comportements avec le temps et la température des largeurs de raie et nombre de spins mesurés, nous avons montré que pour les températures les plus basses (T < ˜ 140 °C) l'isomérisation est incomplète tandis que pour les températures les plus élevées (T > ˜ 200 °C) la dégradation du système devient de plus en plus efficace. Il existe un étroit domaine de température (T ˜ 140 à 150 °C) où des caractéristiques optimales (isomérisation totale + faible dégradation) peuvent être obtenues.

PACS
7630 - Electron paramagnetic resonance and relaxation condensed matter.
8230Q - Isomerization and rearrangement.

Key words
EPR line breadth -- isomer shift -- isomerisation -- polymer films -- EPR study -- cis trans isomerization process -- polyacetylene films