J. Physique Lett. 43, 59-65 (1982)
DOI: 10.1051/jphyslet:0198200430205900

Two-dimensional electronic properties of the purple potassium molybdenum bronze K0.9Mo6O17

R. Buder¹, J. Devenyi¹, J. Dumas¹, J. Marcus¹, J. Mercier¹, C. Schlenker¹ et H. Vincent<sup>2

1</sup>  Groupe des Transitions de Phases, C.N.R.S., B.P. 166, 38042 Grenoble Cedex, France
²  Laboratoire de Cristallographie, C.N.R.S., B.P. 166, 38042 Grenoble Cedex, France

Abstract
The electrical and magnetic properties between 2 K and 300 K, the low temperature specific heat and the crystal structure at 300 K have been studied on single crystals of K0.9Mo6O17 grown by the electrolytic reduction technique. K0.9Mo6O17 is found to be a quasi two-dimensional metal; this is consistent with the structural data. The transition which takes place below 120 K is due to the partial opening of a gap at the Fermi surface, possibly related to the onset of a charge density wave.

Résumé
On a étudié les propriétés électriques et magnétiques entre 2 K et 300 K, la chaleur spécifique à basse température ainsi que la structure cristallographique à 300 K de monocristaux de K0,9Mo6O17, préparés par réduction électrolytique. Cette étude montre que K0,9Mo6O17 est un métal quasi bidimensionnel, ce qui est en bon accord avec les données structurales. La transition observée au-dessous de 120 K est attribuée à l'ouverture d'un gap partiel à la surface de Fermi, probablement associée à l'apparition d'une onde de densité de charge.

PACS
6160 - Crystal structure of specific inorganic compounds.
6540 - Heat capacities of solids.
7215E - Electrical and thermal conduction in crystalline metals and alloys.
7520C - Diamagnetism and paramagnetism in nonmetals.

Key words
crystal atomic structure of inorganic compounds -- electrical conductivity of solids -- Fermi surface -- magnetic susceptibility -- potassium compounds -- specific heat of solids -- thermoelectricity -- 2 to 300K -- susceptibility -- electrical properties -- two dimensional electronic properties -- resistivity -- thermopower -- K sub 0.9 Mo sub 6 O sub 17 -- magnetic properties -- low temperature specific heat -- crystal structure -- single crystals -- quasi two dimensional metal -- Fermi surface -- charge density wave