T.E.M. investigations of room temperature microplasticity in MgAl2O 4 spinel

N. Doukhan

Laboratoire de structure et propriétés de l'état solide, Université de Lille-I, 59655 Villeneuve d'Ascq Cedex, France


Abstract
Dislocations produced by room temperature Vickers indentation on a single crystal of MgO.1.1 Al2O3 spinel have been characterized by T.E.M. These dislocations belong to 1/2 < 110 > { 111 } glide systems. No trace of { 100 } nor { 110 } glide is found. Moreover these dislocations show no preferred orientation nor visible dissociation. However after annealing for 1 day at 1 000 °C, dissociations of the order of 100 Å are observed.


Résumé
On a caractérisé par microscopie électronique les dislocations produites par indentation Vickers à température ambiante sur un monocristal de spinelle MgO.1,1 Al2O3. Ces dislocations appartiennent aux systèmes 1/2 < 110 > { 111 }. On ne détecte aucune trace de glissement dans { 100 } ou { 110 }. En outre ces dislocations ne présentent ni orientation préférentielle, ni dissociation observable. Cependant après recuit de 1 jour à 1000 °C, on observe des dissociations de l'ordre de 100 Å.