J. Physique Lett. 44, 777-784 (1983)
DOI: 10.1051/jphyslet:019830044018077700

Spin glass-like behaviour in the 1D mixed compound CHAC : Mn

A. Cheikhrouhou¹, C. Dupas² et J.P. Renard<sup>2

1</sup>  Faculté des Sciences et Techniques de Sfax, B.P.W., Sfax, Tunisia
²  Institut d'Electronique Fondamentale, Université Paris XI, 91405 Orsay Cedex, France

Abstract
The a.c. susceptibility of the quasi-1D mixed compound C6H 11NH3Cu1-xMnxCl 3 (CHAC : Mn) exhibits at Tmax a frequency dependent maximum. Remanence effects on the magnetization appear below Tmax. The variations with field, time and temperature of the thermoremanent and isothermal remanent magnetizations are similar to those observed in classical spin glasses. These measurements suggest spin glass-like behaviour in linear chains with random exchange at very low impurity concentration.

Résumé
La susceptibilité alternative du composé mixte quasi-1D C6H 11NH3Cu1-xMnxCl 3 (CHAC : Mn) présente à Tmax un maximum dépendant de la fréquence. Des effets de rémanence de l'aimantation apparaissent en dessous de Tmax. Les variations avec le champ, le temps et la température des aimantations thermorémanente et isotherme rémanente sont semblabes à celles des verres de spin classiques. Ces mesures suggèrent un comportement de type verre de spin dans les chaînes linéaires à échange aléatoire à très faible concentration en impuretés.

PACS
7530C - Magnetic moments and susceptibility in magnetically ordered materials.
7540 - Critical point effects, specific heats, short range order in magnetic materials.
7560E - Magnetization curves, hysteresis, Barkhausen and related effects.

Key words
magnetic susceptibility -- manganese -- organic compounds -- remanence -- spin glasses -- hexylammonium trichlorocuprate:Mn -- AC susceptibility -- thermoremanent magnetisation -- isothermal remanent magnetizations -- linear chains -- random exchange -- low impurity concentration