Diffusion Raman spontanée dans (P2O5) x-(SiO2)1-x et (B2 O3)x-(SiO2)1- x

A. Saïssy, J. Botineau, A. Azema et F. Gires

Laboratoire d'Electro-optique, Parc Valrose, 06034 Nice Cedex, France


Abstract
The spontaneous Raman spectra of binary compounds (P2O 5)x-(SiO2)1-x and (B2O3)x-(SiO2) 1-x, prepared by a C.V.D. method, are compared to pure silica spectra in the range 20 to 1 400 cm-1. New characteristic bands occur at 700 cm -1, 1140 cm-1 and 1330 cm-1 for (P2O 5)x-(SiO2)1-x and at 940 cm-1 for (B2O3)x-(SiO 2)1-x with small x. The 700 cm -1 and 1 330 cm-1 bands are used to study the (P2O 5)x-(SiO2)1-x distribution profile in rod preform of optical fibre.


Résumé
Les spectres de diffusion Raman spontanée des composés binaires (P 2O5)x-(SiO2)1- x et (B2O3)x-(SiO 2)1-x, obtenus par dépôt en phase vapeur, sont comparés à celui de la silice pure dans le domaine de 20 à 1 400 cm -1. De nouvelles bandes caractéristiques apparaissent à 700, 1 140 et 1 330 cm-1 pour (P2O5)x-(SiO 2)1-x et à 940 cm-1 pour (B 2O3)x-(SiO2)1- x avec x petit. Les bandes à 700 et 1 330 cm-1 sont utilisées pour étudier le profil de la distribution de (P2O 5)x-(SiO2)1-x dans une préforme de fibre optique.

PACS
4270C - Optical glass.
7830G - Infrared and Raman spectra in inorganic crystals.

Key words
boron compounds -- optical fibres -- optical glass -- phosphorus compounds -- Raman spectra of inorganic solids -- silicon compounds -- P sub 2 O sub 5 sub x SiO sub 2 sub 1 x -- B sub 2 O sub 3 sub x SiO sub 2 sub 1 x -- spontaneous Raman spectra -- 20 to 1400 cm sup 1 -- distribution profile -- rod preform -- optical fibre