J. Physique Lett. 42, 385-388 (1981)
DOI: 10.1051/jphyslet:019810042016038500

Observation of forbidden Bragg reflections in BaMnF4

R. Almairac¹, M. Regis¹, J. Nouet² et C. Filippini<sup>3

1</sup>  Groupe de Dynamique des Phases Condensées (1), U.S.T.L., 34060 Montpellier Cedex, France
²  Laboratoire de Physique de l'Etat Condensé (2), Faculté des Sciences, 72017 Le Mans Cedex, France
³  Institut Max von Laue-Paul Langevin, 156X, 38042 Grenoble Cedex, France

Abstract
Neutron and X-ray technics have been used to show that a weak (100) Bragg reflection appears in BaMnF4 at room temperature, in large samples, i.e. samples used in current experiments (optic, infrared, Raman, neutrons...). The intensity of this reflection increases at low temperature. This effect was not observed in small samples (˜ 0.02 mm3). In a brief discussion we suggest that the space group A21am would not be correct for these large samples of BaMnF4.

Résumé
Des mesures aux R.X. et aux neutrons ont été utilisées pour mettre en évidence une faible tache de Bragg (100) dans BaMnF4, à température ambiante, dans le cas de cristaux présentant un certain volume (comparable à celui utilisé dans les expériences courantes : optique, infrarouge, Raman, neutrons, ...). L'intensité de cette réflexion croit à basse température. Cet effet n'est pas observé dans les petits cristaux (˜ 0,02 mm3). Au cours d'une brève discussion nous suggérons que le groupe d'espace A21am ne serait pas correct pour ces gros échantillons de BaMnF4.

PACS
6112 - Neutron determination of structures.
6160 - Crystal structure of specific inorganic compounds.

Key words
barium compounds -- neutron diffraction examination of materials -- space groups -- X ray diffraction examination of materials -- neutron diffraction -- X ray diffraction -- forbidden Bragg reflections -- BaMnF sub 4 -- room temperature -- low temperature -- space group