Correlation between D.C. bulk conductivity and impurities in undoped poly (p-phenylene)

F. Maurice, G. Froyer, M. Minier et M. Gauneau

Centre National d'Etudes des Télécommunications, Centre Lannion B, Route de Trégastel, B.P. 40, 22301 Lannion, France

Abstract
The D.C. conductivity of non doped poly(p-phenylene) prepared by Kovacic's method fits an Arrhenius law above room temperature. We have correlated the drop of the conductivity during the steps of washing and annealing with the elimination of copper in the material, and we have measured on the purer poly(p-phenylene) a low conductivity of 10-17 (Ω.cm)-1 at 80 °C associated with an activation energy of 1.1 eV.

Résumé
La conductivité continue du poly(p-phénylène) non dopé préparé selon la méthode de Kovacic suit approximativement une loi d'Arrhenius au-dessus de l'ambiante. Nous avons corrélé la chute de conductivité lors des étapes de lavage et de recuit au départ de cuivre, et mesuré sur le produit le plus pur une faible conductivité de 10-17 (Ω.cm)-1 à 80 °C, associée à une énergie d'activation de 1,1 eV.

PACS
7220F - Low field transport and mobility: piezoresistance semiconductors/insulators.
7280L - Electrical conductivity of organic compounds and polymers.

Key words
annealing -- electrical conductivity of amorphous semiconductors and insulators -- impurities -- organic semiconductors -- polymers -- DC bulk conductivity -- impurities -- undoped poly p phenylene -- Kovacic's method -- Arrhenius law -- washing -- annealing -- activation energy