J. Physique Lett. 44, 859-863 (1983)
DOI: 10.1051/jphyslet:019830044020085900

Anisotropy dynamics of CuMn spin glass through torque measurements

J.B. Pastora, T.W. Adair et D.P. Love

Physics Department, Texas A & M University, College Station, Texas 77843, U.S.A.

Abstract
The dynamics of anisotropy energy, (Ea), in a CuMn 0.5 % spin glass sample is investigated by torque measurements. After reducing the cooling field along the Z axis to zero and delaying to allow the time decay of magnetization to diminish, a measuring field H is applied 90° from Z. The anisotropy torque Γ decays due to redefinition of the direction θN of the anisotropy axis N with respect to Z for H ≽ 70 Oe at T = 2.39 K. The angle θN increases with H and T. Ea is found to be unidirectional only.

Résumé
La dynamique de l'énergie d'anisotropie, Ea, est étudiée sur un échantillon de verre de spin CuMn : 0,5 at. % par mesure de couple. Après réduction à zéro du champ de refroidissement dirigé suivant l'axe des Z, et après un délai suffisant pour rendre négligeable l'effet du déclin temporel de l'aimantation, un champ de mesure H est appliqué à un angle de 90° par rapport à l'axe des Z. Le couple d'anisotropie Γ décroît par suite de la redéfinition de la direction θN de l'axe d'anisotropie N par rapport à l'axe des Z pour H ≽ 70 Oe et T = 2,39 K. L'angle θN croit avec H et T. Ea s'avère être unidirectionnelle seulement.

PACS
7530G - Magnetic anisotropy.
7540 - Critical point effects, specific heats, short range order in magnetic materials.

Key words
copper alloys -- magnetic anisotropy -- manganese alloys -- remanence -- spin glasses -- torque -- anisotropy energy dynamics -- remanent magnetisation -- CuMn spin glass -- torque -- cooling field -- time decay of magnetization -- anisotropy torque