J. Physique Lett. 44, 935-945 (1983)
DOI: 10.1051/jphyslet:019830044023093500

Flexible polymers in a nematic medium : ultrasonic measurements

P. Martinoty¹, A. Dubault², C. Casagrande² et M. Veyssié<sup>2

1</sup>  Laboratoire d'Acoustique Moléculaire, Université Louis Pasteur, 4, rue Blaise Pascal, 67070 Strasbourg Cedex, France
²  Laboratoire de Physique de la Matière Condensée, Collège de France, 75231 Paris Cedex 05, France

Abstract
Using a shear wave reflectance technique, two viscosity coefficients in solutions of flexible polymers in a nematic solvent were measured. A large increase in the viscosities was observed when the chains were solubilized in the nematic solvent even at very low concentration. The variation of this effect as a function of the temperature shows the existence of two different situations for the polymer chains. The results are consistent with the theoretical expectations of Brochard.

Résumé
Nous présentons une étude de deux coefficients de friction d'un mélange nématique-polymère, effectuée au moyen de la technique d'absorption des ondes ultrasonores transversales. Les résultats obtenus montrent que la présence du polymère augmente de façon considérable les deux coefficients de friction du nématique pur, bien que les chaînes soient courtes et en faible concentration. Les mesures effectuées en fonction de la température mettent en évidence deux régimes correspondant à des conformations différentes des chaînes polymériques. Ces résultats sont compatibles avec les prévisions théoriques de Brochard.

PACS
6260 - Acoustic properties of liquids.
6620 - Viscosity of liquids: diffusive momentum transport.

Key words
polymer solutions -- ultrasonic reflection -- viscosity of liquids -- ultrasonic measurements -- shear wave reflectance technique -- viscosity coefficients -- flexible polymers -- nematic solvent -- polymer chains