J. Physique Lett. 46, 157-162 (1985)
DOI: 10.1051/jphyslet:01985004604015700

Effects of atomic collisions on rubidium clusters embedded into MgO crystals

M. Treilleux et P. Thévenard

Département de Physique des Matériaux, Université Claude Bernard-Lyon I, 43, boulevard du 11 novembre 1918, 69622 Villeurbanne Cedex, France

Abstract
MgO single crystals, preimplanted with rubidium ions and subsequently annealed, contain small rubidium precipitates which have been well characterized by optical absorption measurements and transmission electron microscopy. Optical absorption measurements have shown that during the reimplantation with Rb + ions the number of precipitates decreases with the fluence : the precipitated phase has completely disappeared for a fluence of 7 x 10 14 ions. cm-2. These effects seem to be associated with an atomic collision process.

Résumé
Des monocristaux de MgO, préimplantés avec des ions rubidium et ensuite recuits, contiennent des petits précipités de rubidium bien caractérisés par mesures d'absorption optique et microscopie électronique en transmission. Des mesures d'absorption optique ont montré que durant la réimplantation avec des ions Rb+ le nombre de précipités diminue avec la dose : la phase précipitée a totalement disparue pour une dose égale à 7 x 10 14 ions.cm-2. Ces effets semblent être associés à un processus de collisions atomiques.

PACS
6170T - Doping and implantation of impurities.
6180J - Ion beam effects.
6475 - Solubility, segregation, and mixing.
7850E - Impurity and defect absorption in insulators.

Key words
annealing -- impurity and defect absorption spectra of inorganic solids -- ion beam effects -- ion implantation -- magnesium compounds -- precipitation -- rubidium -- transmission electron microscope examination of materials -- MgO:Rb sup + -- atomic collisions -- MgO single crystals -- annealed -- optical absorption measurements -- transmission electron microscopy -- reimplantation -- Rb sup + -- precipitates